Water interaction with dental luting cements by means of sorption and solubility

Authors

  • Larissa Pincelli Chaves Paranaense University
  • Fabiana Mezzaroba Ortenzi Graciano North University of Paraná
  • Odair Bim Júnior School of Dentistry of Bauru- University of São Paulo
  • Ana Paula Ribeiro do Vale Pedreira University of Brasilia
  • Adriana Pigozzo Manso University of Bristish Columbia
  • Linda Wang School of Dentistry of Bauru- University of São Paulo

DOI:

https://doi.org/10.14295/bds.2012.v15i4.826

Abstract

Water contributes to the setting reaction of self-adhesive luting cements, however, it can also accelerate their degradation. Objectives: The aim of this study was to compare a self-adhesive resin luting cement to other resin-based and glass-ionomer luting materials with regards to water sorption (WS) and solubility (WSB). The tested null hypothesis was that there is no difference in respect to these properties among the materials. Material and methods: Eight specimens from each group (15 mm x 0.5 mm) were prepared from self-adhesive luting cements Biscem (BC) and RelyX Unicem (R), dual-cure cements Bifix (BF), Allcem (A) and Enforce (E), chemical-cure cements C&B (CB) and Cement Post (CP) and a glass-ionomer luting cement Meron C (M) as the control group. The dual-cure products were light-cured beneath an IPS Empress Esthetic ceramic disk (20 mm x 1.5 mm) and for the chemical reaction materials, a 15 min-interval was respected for removal from the mould. The WS and WSB were respectively calculated as (m2-m3/V) and (m1-m3/V). Mass values of m1, m2 and m3 were determined by cycles of desiccation, water-immersion and a new desiccation. For each property, the data was analyzed by one-criteria ANOVA and Tukey tests (p < 0.05). Results: The glass-ionomer cement presented the highest WS, followed by the self-adhesive luting cements. Other resin cements were less susceptible to WS. No materials differed from each other when the WSB was considered, except for the M, which presented the lowest WSB. Conclusions: Self-adhesive luting cements were more prone to WS since water is essential to their setting reaction. However, their WSB was similar to the other resin-based cements.

Author Biography

Linda Wang, School of Dentistry of Bauru- University of São Paulo

Department of Operative Dentistry, Endodontics and Dental Materials

Downloads

Published

2013-03-04

Issue

Section

Clinical or Laboratorial Research Manuscript