Surface roughness and volumetric contraction of a Y-TZP ceramic sintered by microwave energy and by resistive heating

Autores

  • Nayara Fernanda Barchetta São Paulo State University (Unesp) – Institute of Science and Technology – São José dos Campos – Department of Dental Materials and Prosthodontics – SP – Brazil.
  • Larissa Guazzelli Nanni São Paulo State University (Unesp) – Institute of Science and Technology – São José dos Campos – SP - Brazil.
  • Jean Soares Miranda São Paulo State University (Unesp) – Institute of Science and Technology – São José dos Campos – Department of Dental Materials and Prosthodontics – SP – Brazil.
  • Dolores Ribeiro Ricci Lazar Institute of Energy and Nuclear Research (IPEN) – São Paulo – SP – Brazil.
  • Valter Assui Institute of Energy and Nuclear Research (IPEN) – São Paulo – SP – Brazil.
  • Guilherme de Siqueira Ferreira Anzalone Saavedra São Paulo State University (Unesp) – Institute of Science and Technology – São José dos Campos – Department of Dental Materials and Prosthodontics – SP – Brazil.

DOI:

https://doi.org/10.14295/bds.2017.v20i4.1481

Resumo

Objective: The aim of this study was to evaluate a Y-TZP ceramic sintered by a microwave protocol on volume shrinkage and surface roughness. Material and Methods: Twenty four (N=24) Y-TZP discs were fabricated by milling in CAD/CAM for size standardization. The mean final dimensions of the specimens were 15 mm X 1.6 mm. Samples were divided into 2 groups (n=12): conventional resistive heating sintering protocol (C - Control) and microwave sintering protocol (MO - experimental). For the characterization of the specimens, surface roughness (Ra and Rz parameters) was evaluated with a roughness tester, and volume shrinkage was measured with a hand micrometer. Data were statistically evaluated by Student’s t and Mann-Whitney U tests (?=0.05). Results: The roughness results were: 0.25 ?m ± 0.02 (Ra) and 2.68 ?m ± 0.666 (Rz) for the MO samples; 0.26 ?m ± 0.04 (Ra) and 2.73 ?m ± 0.461 (Rz) for the C group (Ra: p = 0.19; Rz: p = 0.81). The shrinkage results was: MO (21.02% ± 2.70) and C (20.10% ± 0.52) (p = 0.274). Conclusion: The conventional and microwave sintering methods were similar regarding surface roughness and volume shrinkage of Y-TZP dental ceramic.

Keywords

Bioceramics; Microwave sintering; Roughness surface; Zirconia.

Downloads

Não há dados estatísticos.

Downloads

Arquivos adicionais

Publicado

2017-12-15

Como Citar

1.
Barchetta NF, Nanni LG, Miranda JS, Lazar DRR, Assui V, Saavedra G de SFA. Surface roughness and volumetric contraction of a Y-TZP ceramic sintered by microwave energy and by resistive heating. BDS [Internet]. 15º de dezembro de 2017 [citado 11º de setembro de 2025];20(4):124-9. Disponível em: https://ojs.ict.unesp.br/index.php/cob/article/view/1481

Edição

v. 20 n. 4 (2017): Oct. - Dec. / 2017 - Published December 2017

Seção

Artigos de Pesquisa Clínica ou Laboratorial

Licença

TRANSFERÊNCIA DE DIREITOS AUTORAIS E DECLARAÇÃO DE RESPONSABILIDADE



Toda a propriedade de direitos autorais do artigo "____________________________________________________________________" é transferido do autor(es) para a CIÊNCIA ODONTOLÓGICA BRASILEIRA, no caso do trabalho ser publicado. O artigo não foi publicado em outro lugar e não foi submetido simultaneamente para publicação em outra revista.

Vimos por meio deste, atestar que trabalho é original e não apresenta dados manipulados, fraude ou plágio. Fizemos contribuição científica significativa para o estudo e estamos cientes dos dados apresentados e de acordo com a versão final do artigo. Assumimos total responsabilidade pelos aspectos éticos do estudo.



Este texto deve ser impresso e assinado por todos os autores. A versão digitalizada deverá ser apresentada como arquivo suplementar durante o processo de submissão.


Crossref
Scopus
Google Scholar
Europe PMC

Artigos mais lidos pelo mesmo(s) autor(es)